PA66 DP AKV 30 FN00 DUS013 000000德国朗盛Durethan 30%玻纤无卤阻燃尼龙66塑料（18024445500）
PA 66, 30 % glass fibers, injection molding, halogen free flame retardant
ISO Shortname:
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 0.2
C Molding shrinkage, transverse 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 0.7
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 10500 6500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 120 75
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.5 5.1
Izod impact strength 23 °C kJ/m² ISO 180-1U 45 47
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10
Flexural modulus 2 mm/min MPa ISO 178-A 9300 5600
Flexural strength 2 mm/min MPa ISO 178-A 190 120
Flexural strain at flexural strength 2 mm/min % ISO 178-A 2.7 4.8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 120
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 260
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 224
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 >250
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 240
C Burning behavior UL 94 (1.6 mm) 1.5 mm Class UL 94 V-0
Burning behavior UL 94 (UL listed) 0.75 mm Class UL 94 V-0
Burning behavior UL 94 0.4 mm Class UL 94 V-0 |