PA66 A 218 V30 BLACK 21 NS法国罗地亚TECHNYL热稳定尼龙66塑料（18024445500）
TECHNYL A 218 V30 BLACK 21 NS
Properties
Typical values of properties are for natural grades
Standards Unit Values
d.a.m. Cond.
Physical
Water absorption(24h at 23°C) ISO 62 % 0,80
ASTM D-792 % 0,80
Density ISO 1183/A g/cm3 1,37
Molding shrinkage Parallel RHODIA % 0,50
Molding shrinkage normal or perpendicular RHODIA % 0,80
Molding Shrinkage Isotropy RHODIA 0,62
Mechanical
Tensile Modulus ISO 527 Type 1A MPa 10000 7500
Tensile strength at break ISO 527 Type 1A MPa 190 135
Elongation at break ISO 527 Type 1A % 3 6
Flexural modulus ISO 178 MPa 9000 6400
ASTM D-790 MPa 9000
Flexural maximum stress ISO 178 MPa 280 185
ASTM D-790 MPa 290
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 11 15
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 80 88
Izod notched impact strength (23 °C) ISO 180/1A kJ/m2 10 18
ASTM D256 J/m 115
Izod unnotched impact strength ISO 180/1U kJ/m2 60 65
Flammability
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 HB
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 700
Limit Oxygen Index ISO 4589 23
Fire and Smoke index NF F 16 101 I2 / F3
Thermal
Melting Temperature ISO 11357 °C 263
ASTM D3417 °C 260
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 255
Heat deflection temperature (1,82 MPa) ASTM D-648 °C 255
Coef of Linear thermal expansion normal or ISO 11359 E-5/°C 2,5
perpendicular (23°C to 85°C)
Coef of Linear thermal expansion parallel (23°C to ISO 11359 E-5/°C 2,5
85°C)
Electrical
Comparative tracking index (Sol A) IEC 60112 V 600 600
Comparative tracking index (Sol B) IEC 60112 V 500
Dielectric strength IEC 60243 kV/mm 34 29
Dissipation factor IEC 60250 0,010 0,110
Relative permittivity IEC 60250 3,70 4
Surface resistivity IEC 60093 Ohm 6E 14 1E 12
Volume resistivity IEC 60093 Ohm/cm 1E 15 1E 13 |