D862钴基堆焊焊条D862钴基堆焊焊条 型号EDCoCr-E-05
说明适用于高温磨性磨损及细颗粒小角度冲蚀磨损工况。单层堆焊即可满足性能要求,**工作温度1000℃,堆焊层硬度20℃--HRC64-66、工作温度600℃--HRC48-52、工作温度800℃--HRC38-42典型应用领域、工况及部分,炼铁、炼焦、烧洁、水泥等工作领域存在高温磨损的机械设备。FabCO TR-70E70T-1/T-9焊条FabCO TR-70E70T-1/T-9低烟尘、飞溅少、焊接低碳钢及低合金钢。F221喷焊粉F221喷焊粉Cr26 W5 B0.7 Co Rem.HRc 43PTA hardfacing of sealing surface of high temperature and high pressure valve and the edge of hot shearing tool.
高温高压阀门密封面、热剪切刃口的等离子喷焊F223喷焊粉F223喷焊粉Cr21 W5 B1.5 Co Rem.HRc 40PTA hardfacing of parts resistance to wear and corrosion at high temperature, such as valve under high temperature and high pressure, and blower.
高温下耐磨耐蚀件的喷焊,如高温高压阀门、鼓风机F321喷焊粉F321喷焊粉Cr13 B1.5 Si1 Fe Rem.HRc 45PTA hardfacing of corrosion-resistant parts under mid-temperature and mid-pressure, such as stop-plate etc.
中温中压阀门的闸板及其他耐磨件的等离子喷焊
|