25Cr2Ni4WA合金结构钢,伸长率≥11%,硬度≤269HB。化学成份碳 C :0.21~0.28硅 Si:0.17~0.37锰 Mn:0.30~0.60硫 S :允许残余含量≤0.025磷 P :允许残余含量≤0.025铬 Cr:1.35~1.65镍 Ni:4.00~4.50铜 Cu:允许残余含量≤0.025钨 W :0.80~1.20力学性能抗拉强度 σb (MPa):≥1080(110)屈服强度σs (MPa):≥930(95)断面收缩率 ψ (%):≥45冲击功 Akv (J):≥71冲击韧性值 αkv (J/cm2):≥88(9)试样尺寸:试样毛坯尺寸为25mm●热处理规范及金相组织:热处理规范:淬火850℃,油冷;回火550℃,水冷、油冷。18Cr2Ni4WA常见规格:Ф16,Ф18,Ф20,Ф22,Ф25,Ф28,Ф30,Ф35,Ф40,Ф45,Ф50,Ф55,Ф60,Ф65Ф70,Ф75,Ф80,Ф85,Ф90,Ф100,Ф110,Ф120,Ф130,Ф140,Ф150, |