PA66 AKV 50 000000德国朗盛Durethan 50%玻纤注塑尼龙66塑料(18024445500)
PA 66, 50% glass fibers, injection molding
ISO Shortname: ISO 1874-PA 66, GR, 14-160, GF50
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 300 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.23
Molding shrinkage, transverse 150x105x3; 300 °C / MT 80 °C; 400 bar % acc. ISO 2577 1.25
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.02
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.03
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 15700 10700
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 220 170
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.5 4.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 95 95
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 100 100
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 19 23
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 15 15
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 14 18
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 11 11
Flexural modulus 2 mm/min MPa ISO 178-A 14000 10300
Flexural strength 2 mm/min MPa ISO 178-A 370 250
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.0 5.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 235
Ball indentation hardness N/mm² ISO 2039-1 290 160 |