PA66 AKV 35 H2.0 SR1 901510德国朗盛Durethan 35%玻纤热老化稳定尼龙66塑料（18024445500）
PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, improved surface finish
ISO Shortname: ISO 1874-PA 66, GHR, 14-110, GF35
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 300 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.35
Molding shrinkage, transverse 150x105x3; 300 °C / MT 80 °C; 400 bar % acc. ISO 2577 1.4
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.03
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.04
C Molding shrinkage, parallel 60x60x2; 300 °C / MT 80 °C; 600 bar % ISO 294-4 0.32
C Molding shrinkage, transverse 60x60x2; 300 °C / MT 80 °C; 600 bar % ISO 294-4 1.0
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.07
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.09
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 11200 7500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 190 130
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 5.0
C Tensile creep modulus 1 h MPa ISO 899-1 7000
C Tensile creep modulus 1000 h MPa ISO 899-1 5800
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 80 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 70 75
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 12 20
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10 10 |