PA66 AKV 30 HR H2.0 901510德国朗盛Durethan 30%玻纤热老化稳定水解稳定尼龙66塑料（18024445500）
PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilized
ISO/ ASTM
ISO Shortname: ISO 1874-PA 66, GHWR, 14-100, GF30
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.44
C Molding shrinkage, transverse 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.94
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.06
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.12
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9700 6100
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 180 120
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.5 8.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 75 85
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 65 75
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 10 20
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m&sup2; ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 70
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 60
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10 <10
Izod notched impact strength -40 °C kJ/m&sup2; ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 8600 5400
Flexural strength 2 mm/min MPa ISO 178-A 280 180
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 6.5
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 265 150
C Puncture maximum force 23 °C N ISO 6603-2 896 1073
C Puncture maximum force -30 °C N ISO 6603-2 776
C Puncture energy 23 °C J ISO 6603-2 3.1 4.7
C Puncture energy -30 °C J ISO 6603-2 1.9
Ball indentation hardness N/mm&sup2; ISO 2039-1 205 105
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 262
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 245
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 250
C Temperature of deflection under load 8.00 MPa °C ISO 75-1,-2 125
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 254
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.3
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.9
C Burning behavior UL 94 (1.6 mm) 1.6 mm Class UL 94 HB
Burning behavior UL 94 3.2 mm Class UL 94 HB
C Oxygen index Method A % ISO 4589-2 26
Glow wire test (GWFI) 2.0 mm °C IEC 60695-2-12 650
Burning behavior US-FMVSS302 >=1.0 mm ISO 3795 passed
C Vicat softening temperature 50 N; 50 °C/h °C ISO 306 > 230
Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 4.0 12
C Relative permittivity 1 MHz - IEC 60250 3.6 4.5
C Dissipation factor 100 Hz 10-4 IEC 60250 80 3000
C Dissipation factor 1 MHz 10-4 IEC 60250 160 900
C Volume resistivity Ohm·m IEC 60093 1E13 1E09
C Surface resistivity Ohm IEC 60093 1E15 1E13
C Electric strength 1 mm kV/mm IEC 60243-1 35 30
C Comparative tracking index CTI Solution A V IEC 60112 450
Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 5.5
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 2.0
C Density kg/m&sup3; ISO 1183 1360
Bulk density kg/m&sup3; ISO 60 700
Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 290
C Injection molding-Mold temperature °C ISO 294 80
Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax) °C - 280-300
Mold temperature °C - 80-120
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350. |