PA66 AKV 25 F30 000000德国朗盛Durethan 25%玻纤阻燃注塑级尼龙66塑料(18024445500)
PA 66, 25 % glass fibers, injection molding, flame retardant
ISO Shortname: ISO1874-PA 66,GFHR,14-100,GF25; ISO 1043-PA GF FR(17)
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.4
C Molding shrinkage, transverse 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.7
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.3
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 10500 8000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 150 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.2 2.8
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 50 50
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 40 40
Izod impact strength 23 °C kJ/m² ISO 180-1U 45 45
Izod impact strength -30 °C kJ/m² ISO 180-1U 40 40
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 10
Flexural modulus 2 mm/min MPa ISO 178-A 10000 7300
Flexural strength 2 mm/min MPa ISO 178-A 220 160
Flexural strain at flexural strength 2 mm/min % ISO 178-A 2.5 3.5
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 260 |