PA66 DP 2801 000000德国朗盛Durethan无卤阻燃注塑级聚酰胺66尼龙塑料（18024445500）
PA 66, non-reinforced, injection molding, halogen free flame retardant
ISO Shortname: ISO 1874-PA 66, GFHR, 14-030; ISO 1043-PA FR (30)
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 1.14
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 1.22
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.42
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.11
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 3500 1400
C Yield stress 50 mm/min MPa ISO 527-1,-2 94 55
C Yield strain 50 mm/min % ISO 527-1,-2 4.2 20
C Nominal strain at break 50 mm/min % ISO 527-1,-2 10 155
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 80 55
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 11 230
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 110 N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 120 185
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10 15
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 80 N
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 110 130
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 10
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 3200 1300
Flexural strength 2 mm/min MPa ISO 178-A 127 49.0
Flexural strain at flexural strength 2 mm/min % ISO 178-A 6.2 8.0 |