PA66 AC 30 DUS027 000000德国朗盛Durethan耐热耐老化耐冲击尼龙66塑料（18024445500）
PA 66, non-reinforced, injection molding, heat-aging stabilized, improved impact strength
ISO Shortname: ISO 1874-PA 66-HI, GHR, 14-030
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 1.3
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 1.8
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.2
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 3000 1100
C Yield stress 50 mm/min MPa ISO 527-1,-2 70 40
C Yield strain 50 mm/min % ISO 527-1,-2 5.8 25
C Nominal strain at break 50 mm/min % ISO 527-1,-2 18 75
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N N
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10 25
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U N N
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U N N
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 25
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10
Flexural modulus 2 mm/min MPa ISO 178-A 2600 1000
Flexural strength 2 mm/min MPa ISO 178-A 100 40
Flexural strain at flexural strength 2 mm/min % ISO 178-A 6.6 8.8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 80 30
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 261
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 66
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 192
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.8
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 1.1
Other properties (23 °C)
C Density kg/m&sup3; ISO 1183 1110
Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 280
C Injection molding-Mold temperature °C ISO 294 80
Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax) °C - 270-290
admissible residence time at Tmax min - <=10
Mold temperature °C - 80-90
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350. |