¡¡ Technical Properties ¡¡ ¡¡
Physical Typical Value(English) Typical Value (SI) Test Method
Specific Gravity 1.14¡¡ 1.14 g/cm³ ASTM D792
Molding Shrinkage 1.5 to 1.9 % 1.5 to 1.9 % ASTM D955
Mechanical Typical Value(English) Typical Value (SI) Test Method
Tensile Strength2 11600 psi 80.0 MPa ASTM D638
Flexural Modulus3 406000psi 2800 MPa ASTM D790
Flexural Strength3 14500 psi 100 MPa ASTM D790
Impact Typical Value(English) Typical Value (SI) Test Method
Notched Izod Impact ¡¡ ¡¡ ASTM D256
73¡ãF (23¡ãC), 0.126 in (3.20 mm) 0.56 ft¡¤lb/in 30 J/m ¡¡
Thermal Typical Value(English) Typical Value (SI) Test Method
Deflection Temperature Under Load ¡¡ ¡¡ ASTM D648
264(3.20psimm)(1.8 MPa), Unannealed, 0.126 in 149 ¡ãF 65.0 ¡ãC ¡¡
Flammability Typical Value(English) Typical Value (SI) Test Method
Flame Rating (0.126 in (3.20 mm)) V-2¡¡V-2¡¡ Internal Method
¡¡ Processing Information ¡¡ ¡¡
Injection Typical Value(English) Typical Value (SI) ¡¡
Drying Temperature 176 to 194 ¡ãF 80.0 to 90.0 ¡ãC¡¡
Drying Time 4.0 to 6.0 hr 4.0 to 6.0 hr¡¡
Rear Temperature 500 to 536 ¡ãF 260 to 280 ¡ãC¡¡
Middle Temperature 500 to 536 ¡ãF 260 to 280 ¡ãC¡¡
Front Temperature 500 to 536 ¡ãF 260 to 280 ¡ãC¡¡
Mold Temperature 149 to 185 ¡ãF 65.0 to 85.0 ¡ãC |