PA66 RX99518沙伯基础创新耐磨聚酰胺66尼龙塑料（18024445500）
Also known as:LNP™LUBRICOMP™Compound PDX-R-99518
Product reorder name:RX99518
LNP LUBRICOMP RX99518 is a compound based on PA66 containing Proprietary Fillers. Added feature of this material is: Wear Resistant.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, brk, Type I, 5 mm/min
730
kgf/cm²
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min
9.2
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
9.4
%
ASTM D 638
Tensile Modulus, 5 mm/min
32000
kgf/cm²
ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span
29300
kgf/cm²
ASTM D 790
Tensile Stress, yield, 5 mm/min
71
MPa
ISO 527
Tensile Stress, break, 5 mm/min
70
MPa
ISO 527
Tensile Strain, yield, 5 mm/min
9.2
%
ISO 527
Tensile Strain, break, 5 mm/min
9.3
%
ISO 527
Tensile Modulus, 1 mm/min
3180
MPa
ISO 527
Flexural Stress
103
MPa
ISO 178
Flexural Modulus, 2 mm/min
2820
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact, unnotched, 23°C
98
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
5
cm-kgf/cm
ASTM D 256
Multiaxial Impact
7
cm-kgf
ISO 6603
Instrumented Impact Total Energy, 23°C
38
cm-kgf
ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C
58
kJ/m²
ISO 180/1U
Izod Impact, notched 80*10*4 +23°C
5
kJ/m²
ISO 180/1A
THERMAL
Value
Unit
Standard
HDT, 0.45 MPa, 3.2 mm, unannealed
216
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
95
°C
ASTM D 648
CTE, -30°C to 30°C, flow
8.5E-06
1/°C
ASTM D 696
CTE, -30°C to 30°C, xflow
9.2E-06
1/°C
ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
181
°C
ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
73
°C
ISO 75/Af
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.21
-
ASTM D 792
Density
1.21
g/cm³
ASTM D 792
Moisture Absorption, 50% RH, 24 hrs
0.76
%
ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)
1 - 3
%
ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)
2 - 4
%
ASTM D 955
Wear Factor Washer
15
10^-10 in^5-min/ft-lb-hr
ASTM D 3702 Modified
Wear Factor Ring
2
10^-10 in^5-min/ft-lb-hr
ASTM D 3702 Modified
Dynamic COF
0.37
-
ASTM D 3702 Modified
Static COF
0.35
-
ASTM D 3702 Modified
Moisture Absorption (23°C / 50% RH)
1
%
ISO 62
Source GMD, last updated:2013/10/23
Processing
Parameter
Injection Molding
Value
Unit
Drying Temperature
80
°C
Drying Time
4
hrs
Maximum Moisture Content
0.15 - 0.25
%
Melt Temperature
275 - 290
°C
Front - Zone 3 Temperature
295 - 305
°C
Middle - Zone 2 Temperature
280 - 295
°C
Rear - Zone 1 Temperature
265 - 275
°C
Mold Temperature
80 - 95
°C
Back Pressure
0.2 - 0.3
MPa
Screw Speed
30 - 60
rpm
Source GMD, last updated:2013/10/23
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
供应的沙伯基础PA66塑料如下：
LNP™ LUBRICOMP Compound
Grades
Description
RA004
Internally Lubricated Nylon 66 compound containing Aramid.
RAL22
Internally Lubricated Nylon 66 compound containing Aramid, PTFE.
RAL22I
Internally Lubricated, High Impact Nylon 66 compound containing PTFE, Aramid Fiber.
RAL22S
Internally Lubricated Nylon 66 compound containing PTFE, Aramid Fiber.
RAL23
Internally Lubricated Nylon 66 compound containing Aramid Fiber, PTFE.
RAL23S
Heat Stabilized Nylon 66 compound containing Aramid Fiber, PTFE.
RCL36S
Electrically Conductive Nylon 66 compound containing Carbon Fiber, PTFE.
:
RCP36
Electrically Conductive Nylon 66 compound containing Silicone, PTFE, Carbon Fiber.
RFL16
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL26S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing Glass Fiber, PTFE.
RFL33
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL34
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL36L
Internally Lubricated, Low Extractible Nylon 66 compound containing Glass Fiber, PTFE.
RFP36
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RFP36XXZ
PA 66, Silicone, Lubricants, PTFE, Glass, Internally Lubricated, Wear resistant,
RN001S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing MOS2.
RP003
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RP004
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RX01514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX03643H
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX05496
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RX06480
Internally Lubricated Nylon 66 compound containing PTFE, Glass Fiber, Silicone.
RX85514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s). |