PA66 RFP36XXZ沙伯基础创新内部润滑含玻璃纤维有机硅PTFE尼龙66塑料（18024445500）
Also known as:LNP™LUBRICOMP™Compound RFL-4536 LEXBK8-115
Product reorder name:RFP36XXZ
LNP LUBRICOMP RFP36XXZ is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: internally lubricated. Also known as LUBRICOMP RFL-4536 LEX
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, brk, Type I, 5 mm/min
1350
kgf/cm²
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
2.1
%
ASTM D 638
Tensile Modulus, 50 mm/min
106800
kgf/cm²
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
1980
kgf/cm²
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
77200
kgf/cm²
ASTM D 790
Tensile Stress, break, 5 mm/min
135
MPa
ISO 527
Tensile Strain, break, 5 mm/min
2.2
%
ISO 527
Tensile Modulus, 1 mm/min
9400
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
207
MPa
ISO 178
Flexural Modulus, 2 mm/min
9400
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact, unnotched, 23°C
79
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
14
cm-kgf/cm
ASTM D 256
Instrumented Impact Energy @ peak, 23°C
71
cm-kgf
ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C
50
kJ/m²
ISO 180/1U
Izod Impact, notched 80*10*4 +23°C
9
kJ/m²
ISO 180/1A
THERMAL
Value
Unit
Standard
HDT, 1.82 MPa, 3.2mm, unannealed
233
°C
ASTM D 648
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
236
°C
ISO 75/Af
PHYSICAL
Value
Unit
Standard
Density
1.48
g/cm³
ASTM D 792
Moisture Absorption, 50% RH, 24 hrs
0.78
%
ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)
0.2
%
ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)
1
%
ASTM D 955
Wear Factor Washer
11
10^-10 in^5-min/ft-lb-hr
ASTM D 3702 Modified
Dynamic COF
0.56
-
ASTM D 3702 Modified
Static COF
0.46
-
ASTM D 3702 Modified
Density
1.48
g/cm³
ISO 1183
Moisture Absorption (23°C / 50% RH)
1.22
%
ISO 62
Source GMD, last updated:2008/10/30
Processing
Parameter
Injection Molding
Value
Unit
Drying Temperature
80
°C
Drying Time
4
hrs
Maximum Moisture Content
0.15 - 0.25
%
Melt Temperature
280 - 305
°C
Front - Zone 3 Temperature
295 - 305
°C
Middle - Zone 2 Temperature
280 - 295
°C
Rear - Zone 1 Temperature
265 - 275
°C
Mold Temperature
95 - 110
°C
Back Pressure
0.2 - 0.3
MPa
Screw Speed
30 - 60
rpm
Source GMD, last updated:2008/10/30
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
供应的沙伯基础PA66塑料如下：
LNP™ LUBRICOMP Compound
Grades
Description
RA004
Internally Lubricated Nylon 66 compound containing Aramid.
RAL22
Internally Lubricated Nylon 66 compound containing Aramid, PTFE.
RAL22I
Internally Lubricated, High Impact Nylon 66 compound containing PTFE, Aramid Fiber.
RAL22S
Internally Lubricated Nylon 66 compound containing PTFE, Aramid Fiber.
RAL23
Internally Lubricated Nylon 66 compound containing Aramid Fiber, PTFE.
RAL23S
Heat Stabilized Nylon 66 compound containing Aramid Fiber, PTFE.
RCL36S
Electrically Conductive Nylon 66 compound containing Carbon Fiber, PTFE.
:
RCP36
Electrically Conductive Nylon 66 compound containing Silicone, PTFE, Carbon Fiber.
RFL16
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL26S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing Glass Fiber, PTFE.
RFL33
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL34
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL36L
Internally Lubricated, Low Extractible Nylon 66 compound containing Glass Fiber, PTFE.
RFP36
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RFP36XXZ
PA 66, Silicone, Lubricants, PTFE, Glass, Internally Lubricated, Wear resistant,
RN001S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing MOS2.
RP003
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RP004
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RX01514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX03643H
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX05496
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RX06480
Internally Lubricated Nylon 66 compound containing PTFE, Glass Fiber, Silicone.
RX85514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s). |