PA66 RA004沙伯基础创新内部润滑含芳纶聚酰胺66尼龙塑料（18024445500）
Also known as:LNP™LUBRICOMP™Compound RA-1004
Product reorder name:RA004
LNP LUBRICOMP™ RA004 is a compound based on Nylon 66 resin containing Aramid. Added features of this material include: Internally Lubricated.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, break
890
kgf/cm²
ASTM D 638
Tensile Strain, break
4.5
%
ASTM D 638
Flexural Stress
1400
kgf/cm²
ASTM D 790
Flexural Modulus
44900
kgf/cm²
ASTM D 790
IMPACT
Value
Unit
Standard
Izod Impact, unnotched, 23°C
37
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
3
cm-kgf/cm
ASTM D 256
THERMAL
Value
Unit
Standard
HDT, 1.82 MPa, 3.2mm, unannealed
171
°C
ASTM D 648
PHYSICAL
Value
Unit
Standard
Density
1.23
g/cm³
ASTM D 792
Mold Shrinkage, flow, 24 hrs (5)
1.5
%
ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)
2
%
ASTM D 955
Source GMD, last updated:2004/10/07
Processing
Parameter
Injection Molding
Value
Unit
Drying Temperature
80
°C
Drying Time
4
hrs
Maximum Moisture Content
0.15 - 0.25
%
Melt Temperature
275 - 290
°C
Front - Zone 3 Temperature
295 - 305
°C
Middle - Zone 2 Temperature
280 - 295
°C
Rear - Zone 1 Temperature
265 - 275
°C
Mold Temperature
80 - 95
°C
Back Pressure
0.2 - 0.3
MPa
Screw Speed
30 - 60
rpm
Source GMD, last updated:2004/10/07
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
供应的沙伯基础PA66塑料如下：
LNP™ LUBRICOMP Compound
Grades
Description
RA004
Internally Lubricated Nylon 66 compound containing Aramid.
RAL22
Internally Lubricated Nylon 66 compound containing Aramid, PTFE.
RAL22I
Internally Lubricated, High Impact Nylon 66 compound containing PTFE, Aramid Fiber.
RAL22S
Internally Lubricated Nylon 66 compound containing PTFE, Aramid Fiber.
RAL23
Internally Lubricated Nylon 66 compound containing Aramid Fiber, PTFE.
RAL23S
Heat Stabilized Nylon 66 compound containing Aramid Fiber, PTFE.
RCL36S
Electrically Conductive Nylon 66 compound containing Carbon Fiber, PTFE.
:
RCP36
Electrically Conductive Nylon 66 compound containing Silicone, PTFE, Carbon Fiber.
RFL16
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL26S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing Glass Fiber, PTFE.
RFL33
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL34
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL36L
Internally Lubricated, Low Extractible Nylon 66 compound containing Glass Fiber, PTFE.
RFP36
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RFP36XXZ
PA 66, Silicone, Lubricants, PTFE, Glass, Internally Lubricated, Wear resistant,
RN001S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing MOS2.
RP003
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RP004
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RX01514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX03643H
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX05496
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RX06480
Internally Lubricated Nylon 66 compound containing PTFE, Glass Fiber, Silicone.
RX85514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s). |