PA66 135F NC010美国杜邦Zytel® 聚酰胺66尼龙塑料（18024445500）
Zytel® 135F is a nucleated polyamide 66 resin for injection moulding. It was developed for fast cycles and high productivity.
General information Value Unit Test Standard
Resin Identification PA66 - -
Part Marking Code >PA66< - ISO 11469
Rheological properties dry / cond Unit Test Standard
Viscosity number 150 / * cm&sup3;/g ISO 307, 1157, 1628
Moulding shrinkage, parallel 0.7 / * % ISO 294-4, 2577
Moulding shrinkage, normal 1.3 / * % ISO 294-4, 2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 3600 / 2000 MPa ISO 527-1/-2
Yield stress 98 / 67 MPa ISO 527-1/-2
Yield strain 4.5 / 18 % ISO 527-1/-2
Nominal strain at break 13 / 50 % ISO 527-1/-2
Strain at Break, 23°C, 50mm/min 20 / >50 % ISO 527-1/-2
Tensile creep modulus ISO 899-1
1h * / 2000 MPa
1000h * / 1280 MPa
Charpy impact strength ISO 179/1eU
23°C N / N kJ/m&sup2;
-30°C N / N kJ/m&sup2;
Charpy notched impact strength ISO 179/1eA
23°C 4 / 9 kJ/m&sup2;
-30°C 3 / 2.5 kJ/m&sup2;
Izod notched impact strength ISO 180/1A
23°C 3.5/9 kJ/m&sup2;
-30°C 3/2 kJ/m&sup2;
Hardness, Rockwell, M-scale 87/64 - ISO 2039-2
Hardness, Rockwell, R-scale 123/116 - ISO 2039-2
Thermal properties dry/cond Unit Test Standard
Melting temperature, 10°C/min 263/* °C ISO 11357-1/-3
Glass transition temperature, 10°C/min 60/- °C ISO 11357-1/-2
Temp. of deflection under load ISO 75-1/-2
1.8 MPa 75 / * °C
0.45 MPa 210 / * °C
Vicat softening temperature, 50°C/h, 50N 245 / * °C ISO 306
Coeff. of linear therm. expansion, parallel 121 / * E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion, normal 121 / * E-6/K ISO 11359-1/-2
Thermal conductivity of melt 0.16 W/(m K) -
Spec. heat capacity of melt 2790 J/(kg K) -
RTI, electrical, 0.75 mm 130 / * °C UL 746B
RTI, impact, 0.75 mm 75 °C UL 746B
RTI, strength, 0.75 mm 85 °C UL 746B
Flammability dry/cond Unit Test Standard
Burning Behav. at 1.5mm nom. thickn. V-2/* class IEC 60695-11-10
Thickness tested 1.5/* mm IEC 60695-11-10
UL recognition UL/* - -
Burning Behav. at thickness h V-2/* class IEC 60695-11-10
Thickness tested 0.71/* mm IEC 60695-11-10
Glow Wire Flammability Index IEC 60695-2-1/2
0.75mm 960 / - °C
1.5mm 960 / - °C
3mm 960 / - °C
Glow Wire Ignition Temperature IEC 60695-2-1/3
0.75mm 725/- °C
1.5mm 750/- °C
3mm 800/- °C
Electrical properties dry/cond Unit Test Standard
Relative permittivity IEC 60250
100Hz 3.9 / 8.7 -
1MHz 3.8 / 3.9 -
Dissipation factor IEC 60250
100Hz 70 / 2400 E-4
1MHz 200 / 600 E-4
Comparative tracking index 600 / - - IEC 60112
Other properties dry / cond Unit Test Standard
Humidity absorption, 2mm 2.7 / * % Sim. to ISO 62
Water absorption, 2mm 8.5 / * % Sim. to ISO 62
Density 1140 / - kg/m&sup3; ISO 1183
Density of melt 1010 kg/m&sup3; -
Film Properties dry / cond Unit Test Standard
Strain at yield, parallel 4.5 / * % ISO 527-3 |