PA66 80G33HS1L NC010美国杜邦Zytel® 33%玻纤增强抗冲击性聚酰胺66尼龙塑料（18024445500）
Zytel® 80G33HS1L NC010 is a 33% glass fiber reinforced heat stabilized polyamide 66 resin with outstanding impact resistance developed
using DuPont Super Tough technology.
General information Value Unit Test Standard
Resin Identification PA66-IGF33 - -
Part Marking Code >PA66-IGF33< - ISO 11469
Rheological properties dry / cond Unit Test Standard
Viscosity number 160 / * cm&sup3;/g ISO 307, 1157, 1628
Moulding shrinkage, parallel 0.3 / * % ISO 294-4, 2577
Moulding shrinkage, normal 0.7 / * % ISO 294-4, 2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 8900 / 6200 MPa ISO 527-1/-2
Stress at break 146 / 108 MPa ISO 527-1/-2
Strain at break 3.7 / 7 % ISO 527-1/-2
Flexural Modulus 7500 / 6200 MPa ISO 178
Tensile creep modulus ISO 899-1
1h * / 5300 MPa
1000h * / 4300 MPa
Charpy impact strength ISO 179/1eU
23°C 97 / 98 kJ/m&sup2;
-30°C 106 / 100 kJ/m&sup2;
Charpy notched impact strength ISO 179/1eA
23°C 20 / 28 kJ/m&sup2;
-30°C 18 / 17 kJ/m&sup2;
-40°C 14 / 18 kJ/m&sup2;
Izod notched impact strength ISO 180/1A
23°C 21 / 26 kJ/m&sup2;
-30°C 17 / 16 kJ/m&sup2;
-40°C 15 / 15 kJ/m&sup2;
Izod impact strength ISO 180/1U
23°C 80/80 kJ/m&sup2;
-30°C 80/75 kJ/m&sup2;
Hardness, Rockwell, M-scale 70/- - ISO 2039-2
Hardness, Rockwell, R-scale 110/- - ISO 2039-2
Thermal properties dry/cond Unit Test Standard
Melting temperature, 10°C/min 262/* °C ISO 11357-1/-3
Glass transition temperature, 10°C/min 75/- °C ISO 11357-1/-2
Temp. of deflection under load ISO 75-1/-2
1.8 MPa 246/* °C
0.45 MPa 261/* °C
Vicat softening temperature, 50°C/h, 50N 245/* °C ISO 306
Coeff. of linear therm. expansion, parallel 15/* E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion, normal 119/* E-6/K ISO 11359-1/-2
Thermal conductivity of melt 0.22 W/(m K) -
Spec. heat capacity of melt 2200 J/(kg K) -
Eff. thermal diffusivity m&sup2;/s -
RTI, electrical, 0.75 mm 130 / * °C UL 746B
RTI, impact UL 746B
0.75 mm 65 °C
1.5mm 105 / * °C
RTI, strength UL 746B
0.75 mm 85 °C
1.5mm 95 / * °C
3mm 105 °C
Flammability dry / cond Unit Test Standard
Burning Behav. at 1.5mm nom. thickn. HB / * class IEC 60695-11-10
Thickness tested 1.5 / * mm IEC 60695-11-10
UL recognition UL / * - -
Burning Behav. at thickness h HB / * class IEC 60695-11-10
Thickness tested 0.75 / * mm IEC 60695-11-10
Electrical properties dry / cond Unit Test Standard
Relative permittivity, 1MHz 3.6 / 4.3 - IEC 60250
Dissipation factor, 1MHz 130 / 600 E-4 IEC 60250
Volume resistivity >1E13 / 1E9 Ohm*m IEC 60093
Surface resistivity * / 1E12 Ohm IEC 60093
Comparative tracking index 400 / - - IEC 60112
Other properties dry / cond Unit Test Standard
Humidity absorption, 2mm 1.5 / * % Sim. to ISO 62
Water absorption, 2mm 4.5 / * % Sim. to ISO 62
Density 1330 / - kg/m&sup3; ISO 1183
Density of melt 1120 kg/m&sup3; -
Water Absorption, Immersion 24h 0.85 / * % ASTM D 570 |