Zytel® 80G14AHS NC010 is a 14% glass fiber reinforced, toughened, high flow, heat stabilised polyamide 66 resin. It offers outstanding
performance in injection moulding applications.
General information Value Unit Test Standard
Resin Identification PA66-IGF14 - -
Part Marking Code >PA66-IGF14< - ISO 11469
Rheological properties dry / cond Unit Test Standard
Moulding shrinkage, parallel 0.7 / * % ISO 294-4, 2577
Moulding shrinkage, normal 0.8 / * % ISO 294-4, 2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 5000 / 3300 MPa ISO 527-1/-2
Stress at break 110 / 72 MPa ISO 527-1/-2
Strain at break 3.8 / 9 % ISO 527-1/-2
Flexural Modulus 4400 / 3120 MPa ISO 178
Charpy impact strength ISO 179/1eU
23°C 73 / 76 kJ/m&sup2;
-30°C - / 71 kJ/m&sup2;
Charpy notched impact strength ISO 179/1eA
23°C 13 / 17 kJ/m&sup2;
-30°C 9 / 7 kJ/m&sup2;
-40°C - / 6 kJ/m&sup2;
Izod notched impact strength ISO 180/1A
23°C 13/- kJ/m&sup2;
-40°C 6/- kJ/m&sup2;
Thermal properties dry/cond Unit Test Standard
Melting temperature, 10°C/min 263/* °C ISO 11357-1/-3
Temp. of deflection under load ISO 75-1/-2
1.8 MPa 240/* °C
0.45 MPa 221/* °C
Vicat softening temperature, 50°C/h, 50N 215/* °C ISO 306
Coeff. of linear therm. expansion, parallel 40/* E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion, normal 120/* E-6/K ISO 11359-1/-2
Flammability dry/cond Unit Test Standard
Burning Behav. at 1.5mm nom. thickn. HB/* class IEC 60695-11-10
Thickness tested 1.5/* mm IEC 60695-11-10
Burning Behav. at thickness h HB/* class IEC 60695-11-10
Thickness tested 0.75/* mm IEC 60695-11-10
Burning rate, Thickness 1 mm 44 mm/min ISO 3795 (FMVSS 302)
Electrical properties dry / cond Unit Test Standard
Dissipation factor, 100Hz 270 / 180 E-4 IEC 60250
Other properties dry / cond Unit Test Standard
Humidity absorption, 2mm 1.9 / * % Sim. to ISO 62
Density 1190 / - kg/m&sup3; ISO 1183 |