PA66 PA66-CF40-02 AF3004 Natural美国泰科纳CELSTRAN 40%长碳纤 PA66 PA66-CF40-02 AF3004 Natural美国泰科纳CELSTRAN 40%长碳纤维增强18024445500
40% long carbon fiber reinforced Nylon 6/6
Physical properties Value Unit Test Standard
Density 1340 kg/m³ ISO 1183
Mold shrinkage - parallel 0.0005 % ISO 294-4
Mold shrinkage - normal 0.003 % ISO 294-4
PA66 PA66-GF20-02P11/12美国泰科纳CELSTRAN 20%长玻纤增强尼龙6 PA66 PA66-GF20-02P11/12美国泰科纳CELSTRAN 20%长玻纤增强尼龙66塑料18024445500
Physical properties Value Unit Test Standard
Density 1300 kg/m³ ISO 1183
Mechanical properties Value Unit Test Standard
Tensile modulus 1mm/min 8300 MPa ISO 527-2/1A
Tensile modulus 80°C 4970 MPa ISO 527-2/1A
Tensile strength 80°C 103 MPa ISO 527-2/1A
PA66 PA66-GF30-07美国泰科纳CELSTRAN流动增强30%玻纤增强 PA66 PA66-GF30-07美国泰科纳CELSTRAN流动增强30%玻纤增强18024445500
30% Long Glass Reinforced, Flow Enhanced, Nylon 66
Physical properties Value Unit Test Standard
Density 1360 kg/m³ ISO 1183
Mechanical properties Value Unit Test Standard
Tensile modulus 1mm/min 9500 MPa ISO 527-2/1A
Tensile stress at break 5mm/min 160 MPa ISO 527-2/1A
Tensile strain at break 5mm/min 1.91 % ...
PA66 PA66-GF40-01美国泰科纳CELSTRAN 40%波玻纤增强尼龙66塑料 PA66 PA66-GF40-01美国泰科纳CELSTRAN 40%波玻纤增强尼龙66塑料18024445500
Mechanical properties Value Unit Test Standard
Tensile modulus 80°C 7800 MPa ISO 527-2/1A
Tensile strength 80°C 135 MPa ISO 527-2/1A
Elongation at break 80°C 2.5 % ISO 527-2/1A
Flexural modulus 23°C 11100 MPa ISO 178
Flexural modulus 80°C 7200 MPa ISO 178
Flexural strength 23°C 300 MPa ISO 178
PA66 PA66-GF40-02P11美国泰科纳CELSTRAN 40%长玻纤增强 PA66 PA66-GF40-02P11美国泰科纳CELSTRAN 40%长玻纤增强18024445500
Mechanical properties Value Unit Test Standard
Tensile modulus 1mm/min 13000 MPa ISO 527-2/1A
Tensile stress at break 5mm/min 215 MPa ISO 527-2/1A
Tensile strain at break 5mm/min 2 % ISO 527-2/1A
Flexural modulus 23°C 8100 MPa ISO 178
Flexural strength 23°C 200 MPa ISO 178