PC 141沙伯基础创新LEXAN Resin非卤化聚碳酸酯（13422875056）
Nonhalogenated. 10.5 MFR.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 50 mm/min
630
kgf/cm²
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
700
kgf/cm²
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
7
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
130
%
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
980
kgf/cm²
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
23900
kgf/cm²
ASTM D 790
Hardness, Rockwell M
70
-
ASTM D 785
Hardness, Rockwell R
118
-
ASTM D 785
Taber Abrasion, CS-17, 1 kg
10
mg/1000cy
ASTM D 1044
IMPACT
Value
Unit
Standard
Izod Impact, unnotched, 23°C
326
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
81
cm-kgf/cm
ASTM D 256
Tensile Impact, Type S
589
cm-kgf/cm²
ASTM D 1822
Falling Dart Impact (D 3029), 23°C
1728
cm-kgf
ASTM D 3029
Instrumented Impact Energy @ peak, 23°C
650
cm-kgf
ASTM D 3763
THERMAL
Value
Unit
Standard
Vicat Softening Temp, Rate B/50
154
°C
ASTM D 1525
HDT, 0.45 MPa, 6.4 mm, unannealed
137
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed
132
°C
ASTM D 648
CTE, -40°C to 95°C, flow
6.84E-05
1/°C
ASTM E 831
Specific Heat
1.25
J/g-°C
ASTM C 351
Thermal Conductivity
0.27
W/m-°C
ASTM C 177
Relative Temp Index, Elec
130
°C
UL 746B
Relative Temp Index, Mech w/impact
130
°C
UL 746B
Relative Temp Index, Mech w/o impact
130
°C
UL 746B
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.2
-
ASTM D 792
Specific Volume
0.83
cm³/g
ASTM D 792
Density
1.19
g/cm³
ASTM D 792
Water Absorption, 24 hours
0.15
%
ASTM D 570
Water Absorption, equilibrium, 23C
0.35
%
ASTM D 570
Water Absorption, equilibrium, 100°C
0.58
%
ASTM D 570
Mold Shrinkage, flow, 3.2 mm (5)
0.5 - 0.7
%
SABIC Method
Melt Flow Rate, 300°C/1.2 kgf
10.5
g/10 min
ASTM D 1238
OPTICAL
Value
Unit
Standard
Light Transmission, 2.54 mm
88
%
ASTM D 1003
Haze, 2.54 mm
1
%
ASTM D 1003 |