PA6 C 218 MZ20 V10 BLACK Z法国罗地亚TECHNYL热稳定注塑级20%矿物填充10%玻纤(18024445500)
Properties Standards Unit Values
d.a.m*. Cond.**
Physical
Density ISO 1183-A g/cm3 1.36 -
Molding shrinkage Parallel (1) (RHODIA-EP) RHODIA-EP % 0.54 -
Molding shrinkage normal or perpendicular (1) (Rhodia EP) RHODIA-EP % 0.95 -
Molding Shrinkage Isotropy (Rhodia EP) RHODIA-EP 0.57 -
Mechanical
Tensile modulus ISO 527 type 1 A MPa 7400 4500
Elongation at break ISO 527 type 1 A % 3.30 5.5
Tensile strength at break ISO 527 type 1 A MPa 100 60
Flexural modulus ISO 178 MPa 9300 -
Flexural maximum stress ISO 178 MPa 255 -
Charpy notched impact strength ISO 179/1eA kJ/m2 14.10 10
Charpy unnotched impact strength ISO 179/1eU kJ/m2 60 85
Charpy unnotched impact strength ISO 179/1eU kJ/m2 92 -
Izod notched impact strength ISO 180/1A kJ/m2 15 -
Izod unnotched impact strength ISO 180/1U kJ/m2 82 -
Thermal
Melting Temperature ISO 11357 °C 222 -
Heat deflection temperature, 1,8 Mpa ISO 75/Af °C 205 - |