PA6 C 216 V30 NATURAL法国罗地亚TECHNYL注塑级30%玻纤增强尼龙6塑料(18024445500)
Standards Unit Values
d.a.m. Cond.
Physical
Water absorption(24h at 23°C) ISO 62 % 1,05
Density ISO 1183/A g/cm3 1,36
Molding shrinkage Parallel ISO 294-4 % 0,65
Molding shrinkage normal or perpendicular ISO 294-4 % 0,35
Mechanical
Tensile Modulus ISO 527 Type 1A MPa 9600 6200
Tensile strength at break ISO 527 Type 1A MPa 190 110
Elongation at break ISO 527 Type 1A % 3,80 4,50
Flexural modulus ISO 178 MPa 8400 4900
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 15 31,5
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 100 108
Izod notched impact strength (23 °C) ASTM D256 J/m 120
ISO 180/1A kJ/m2 14 24
Flammability
Flammability (Thickness: 0,8 mm) ISO 1210 / UL94 HB
Flammability (Thickness: 3,2 mm) ISO 1210 / UL94 HB
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 650
Limit Oxygen Index ISO 4589 23
Thermal
Melting Temperature ISO 11357 °C 222
Heat deflection temperature (1,82 MPa) ASTM D-648 °C 210
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 205
Coef of Linear thermal expansion parallel (23°C to ISO 11359 E-5/°C 3,2 |