PA6 DP BM 65 X FM30 901510德国朗盛Durethan 65%矿物/玻纤无卤阻燃尼龙6塑料（18024445500）
PA 6, 65 % mineral/glass fibers, injection molding, halogen free flame retardant, improved flowability despite the high degree of filling
ISO Shortname: ISO 1874-PA 6, GFHR, 14-120, (MD+GF) 65; ISO 1043-PA (MD+GF) FR (61)
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 500 bar % ISO 294-4 0.4
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 500 bar % ISO 294-4 0.5
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 12100 6000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 120 73
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 1.6 2.2
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 30 23
Izod impact strength 23 °C kJ/m² ISO 180-1U 25 22
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 12300 6000
Flexural strength 2 mm/min MPa ISO 178-A 175 110
Flexural strain at flexural strength 2 mm/min % ISO 178-A 1.8 2.6
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 220
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 181
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 200
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 204
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.3 |