PA6 BM 230 H2.0 901510µÂ¹úÀÊÊ¢Durethan 30%¿óÎïÄÍÈÈÀÏ»¯Îȶ¨ÄáÁú6ËÜÁÏ£¨18024445500£©
PA 6, injection molding, 30 % mineral, isotropic properties, heat-aging stabilized
ISO/ ASTM
ISO Shortname: ISO 1874-PA 6, MHR, 14-050, MD30
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 ¡ãC / MT 80 ¡ãC; 500 bar % acc. ISO 2577 1.08¡¡
Molding shrinkage, transverse 150x105x3; 280 ¡ãC / MT 80 ¡ãC; 500 bar % acc. ISO 2577 1.12¡¡
Post- shrinkage, parallel 150x105x3; 120 ¡ãC; 4 h % acc. ISO 2577 0.32¡¡
Post- shrinkage, transverse 150x105x3; 120 ¡ãC; 4 h % acc. ISO 2577 0.3¡¡
Mechanical properties (23 ¡ãC/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 5000 2000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 80 50
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 10 45
C Charpy impact strength 23 ¡ãC kJ/m² ISO 179-1eU 120 N
C Charpy impact strength -30 ¡ãC kJ/m² ISO 179-1eU 80 80
C Charpy notched impact strength 23 ¡ãC kJ/m&sup2; ISO 179-1eA < 10 13
C Charpy notched impact strength -30 ¡ãC kJ/m&sup2; ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 ¡ãC kJ/m&sup2; ISO 179-1eA < 10 < 10
Izod impact strength 23 ¡ãC kJ/m&sup2; ISO 180-1U 122 N
Izod impact strength -30 ¡ãC kJ/m&sup2; ISO 180-1U 80 95
Izod notched impact strength -30 ¡ãC kJ/m&sup2; ISO 180-1A < 10 < 10
Izod notched impact strength -40 ¡ãC kJ/m&sup2; ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 4700 1800
Flexural strength 2 mm/min MPa ISO 178-A 140 60
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.5 8.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 130 55 |