PA6 BTC 65 H3.0 EF 901510德国朗盛Durethan 65%矿物热传导性改进尼龙6塑料（18024445500）
PA 6, 65% mineral, injection molding, improved heat conductivity
ISO Shortname: ISO 1874-PA6, GHR, 10-090, MD65
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.66
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.68
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.16
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.18
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9900 3500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 90 45
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3 4.5
Izod impact strength 23 °C kJ/m² ISO 180-1U 35 25
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 10200
Flexural strength 2 mm/min MPa ISO 178-A 150
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3 |