PA6 BKV 25 H2.0 LT 904040德国朗盛Durethan 25%玻纤增强热老化稳定尼龙6塑料（18024445500）
PA 6, 25 % glass fibers, injection molding, heat-aging stabilized, laser-transparent, IR-transparent black pigmentation
ISO Shortname: ISO 1874-PA 6, GHR, 14-080, GF25
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.21
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.88
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.04
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.14
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 8400 5100
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 160 90
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 6.0
C Tensile creep modulus 1 h MPa ISO 899-1 4500
C Tensile creep modulus 1000 h MPa ISO 899-1 3500
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 60 80
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 45 45
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10 10
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10 <10
Charpy notched impact strength -40 °C kJ/m&sup2; ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 65 85
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 60 65
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10 <10
Izod notched impact strength -40 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 7200 4200
Flexural strength 2 mm/min MPa ISO 178-A 250 145 |