PA6 BKV 215 H2.0 DUS035 900051德国朗盛Durethan 15%玻纤热老化稳定尼龙6塑料（18024445500）
PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized
ISO Shortname: ISO 1874-PA 6/66-HI, GHR, 14-040, GF15
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.5
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.8
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 4300 2100
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 85 55
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 4.5 15
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 70 110
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 80 80
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 20 35
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 60 90
Izod impact strength -30 °C kJ/m² ISO 180-1U 65 60
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 20 35
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 10 10
Flexural modulus 2 mm/min MPa ISO 178-A 4000 2000
Flexural strength 2 mm/min MPa ISO 178-A 135 70
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.5 8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 120 55
C Puncture maximum force 23 °C N ISO 6603-2 1500
C Puncture maximum force -30 °C N ISO 6603-2 750
C Puncture energy 23 °C J ISO 6603-2 10
C Puncture energy -30 °C J ISO 6603-2 4
Ball indentation hardness N/mm² ISO 2039-1 120 |