PA6 BKV 20 FN01 000000德国朗盛Durethan 18%玻纤增强无卤阻燃尼龙6塑料（18024445500）
PA 6, 18 % glass fibers, injection molding, halogen free flame retardant
ISO Shortname: ISO 1874-PA 6, GFHR, 12-080, GF18; ISO 1043-PA GF FR (30+40+72)
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Melt volume-flow rate 260 °C; 5 kg cm³/(10 min) ISO 1133-1 37
C Molding shrinkage, parallel 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.3
C Molding shrinkage, transverse 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.6
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 7960 4500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 110 60
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 4.9
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 50 60
Izod impact strength 23 °C kJ/m² ISO 180-1U 40 45
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 12
Flexural modulus 2 mm/min MPa ISO 178-A 7200 4200
Flexural strength 2 mm/min MPa ISO 178-A 170 110
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.2 6.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 95
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 222
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 200
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 218
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 205
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.3
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.9
C Burning behavior UL 94 0.75 mm Class UL 94 V-0
C Burning behavior UL 94 1.5 mm Class UL 94 V-0
C Burning behavior UL 94 3.0 mm Class UL 94 5VA
C Oxygen index Method A % ISO 4589-2 34
Glow wire test (GWFI) 0.8 mm °C IEC 60695-2-12 960
Glow wire test (GWFI) 1.5 mm °C IEC 60695-2-12 960
Glow wire test (GWFI) 3.0 mm °C IEC 60695-2-12 960
Glow wire test (GWIT) 0.75 mm °C IEC 60695-2-13 750
Glow wire test (GWIT) 1.5 mm °C IEC 60695-2-13 750
Glow wire test (GWIT) 3.0 mm °C IEC 60695-2-13 750
Electrical properties (23 °C/50 % r. h.)
C Volume resistivity Ohm·m IEC 60093 5.3E15
C Surface resistivity Ohm IEC 60093 8.6E15
Comparative tracking index CTI Solution A Rating UL 746A 0
Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 5.3
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 1.6
C Density kg/m&sup3; ISO 1183 1340
Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 260
C Injection molding-Mold temperature °C ISO 294 80
Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.07
Melt temperature (Tmin - Tmax) °C - 250-270
Mold temperature °C - 80
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350. |