PA6 DP 2131/20 H3.0 000000德国朗盛Durethan 20%玻纤增强热老化稳定耐候尼龙6塑料（18024445500）
PA 6, 20 % glass fibers, injection molding, heat-aging stabilized, weather stabilized, improved surface finish
ISO Shortname: ISO 1874 PA 6, GHR, 14-080, GF20
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.3
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.7
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 7600 4700
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 150 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3 7
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 45 60
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 40 40
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10 <10
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 30 45
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 30 30
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 < 10
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 6400 4100
Flexural strength 2 mm/min MPa ISO 178-A 210 130
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4 6.5
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 195 110
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 222
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 195
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 215
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.2
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.9
Other properties (23 °C)
C Density kg/m&sup3; ISO 1183 1280
Bulk density kg/m&sup3; ISO 60 700
Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 280
C Injection molding-Mold temperature °C ISO 294 80
Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax) °C - 270-290
Mold temperature °C - 80-120
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350. |