PA6 BKV 55 TPX 900116德国朗盛Durethan 55%玻纤增强热老化稳定流动性改进尼龙6塑料（18024445500）
PA 6, 55 % glass fibers, injection molding, improved flowability, heat-aging stabilized
ISO Shortname: ISO1874: PA6, GHR, 10-190, GF55
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.2
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.5
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 17300 10500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 215 140
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.5 3.5
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 90 85
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15 20
Izod impact strength 23 °C kJ/m² ISO 180-1U 90 85
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15 20
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 15 20
Flexural modulus 2 mm/min MPa ISO 178-A 16500 11000
Flexural strength 2 mm/min MPa ISO 178-A 330 210
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3 3.5
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 210
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 221
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 208
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 218
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.12
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.9
Other properties (23 °C)
C Density kg/m³ ISO 1183 1620
Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 280
C Injection molding-Mold temperature °C ISO 294 80
Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax) °C - 270-290
Mold temperature °C - 80-120
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350. |