PA6 BKV 50 H2.0 EF DUS030 901510德国朗盛Durethan 50%玻纤增强流动性改进尼龙6塑料（18024445500）
PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized
ISO Shortname: ISO1874-PA 6, GHR, 10-160, GF50
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.20
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.60
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.10
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 16000 9000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 215 130
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.5 4
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 90 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 90
Izod impact strength 23 °C kJ/m² ISO 180-1U 80 80
Izod impact strength -30 °C kJ/m² ISO 180-1U 80
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 15
Flexural modulus 2 mm/min MPa ISO 178-A 15000 9500
Flexural strength 2 mm/min MPa ISO 178-A 320 205
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.0 4.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 200
C Puncture maximum force 23 °C N ISO 6603-2 1000
C Puncture maximum force -30 °C N ISO 6603-2 900
C Puncture energy 23 °C J ISO 6603-2 3.7
C Puncture energy -30 °C J ISO 6603-2 3.5
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 220
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 213
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 220
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.1
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.8
Other properties (23 °C)
C Density kg/m³ ISO 1183 1570
Bulk density kg/m³ ISO 60 700
Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 280
C Injection molding-Mold temperature °C ISO 294 80
Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax) °C - 270-290
Mold temperature °C - 80-120
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350. |