PA6 BKV 50 H2.0 EF 900116德国朗盛Durethan 50%玻纤增强尼龙6塑料（18024445500）
PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized
ISO Shortname: ISO1874-PA 6, GHR, 10-160, GF50
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.19
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.6
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.04
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.08
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 16200 10000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 215 140
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.7 3.5
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 100 85
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 95 85
Izod impact strength 23 °C kJ/m² ISO 180-1U 85 80
Izod impact strength -30 °C kJ/m² ISO 180-1U 85 80
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 17 20
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 15
Flexural modulus 2 mm/min MPa ISO 178-A 15000 9900
Flexural strength 2 mm/min MPa ISO 178-A 340 230
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.1 4.4
C Puncture maximum force 23 °C N ISO 6603-2 1179
C Puncture maximum force -30 °C N ISO 6603-2 1000
C Puncture energy 23 °C J ISO 6603-2 4.3
C Puncture energy -30 °C J ISO 6603-2 3.4
Ball indentation hardness N/mm² ISO 2039-1 232 |