PA6 BKV 50 H2.0 901510德国朗盛Durethan 50%玻纤增强尼龙6塑料（18024445500）
PA 6, 50 % glass fibers, injection molding, heat-aging stabilized
ISO/ ASTM
ISO Shortname: ISO 1874-PA 6, GHR, 14-160, GF50
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.16
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.85
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.02
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.05
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 16300 9800
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 220 140
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 5.0
C Tensile creep modulus 1 h MPa ISO 899-1 8100
C Tensile creep modulus 1000 h MPa ISO 899-1 6600
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 100 100
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 85 80
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 20 25
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 15 13
Izod impact strength 23 °C kJ/m² ISO 180-1U 85 85
Izod impact strength -30 °C kJ/m² ISO 180-1U 80 80
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 20 25
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 12 12
Flexural modulus 2 mm/min MPa ISO 178-A 15100 9700
Flexural strength 2 mm/min MPa ISO 178-A 360 230
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.0 5.0
C Puncture maximum force 23 °C N ISO 6603-2 1200
C Puncture maximum force -30 °C N ISO 6603-2 1060
C Puncture energy 23 °C J ISO 6603-2 4.2 8.9
C Puncture energy -30 °C J ISO 6603-2 3.7
Ball indentation hardness N/mm² ISO 2039-1 250 109 |