PA6 BKV 50 G H2.0 EF 000000德国朗盛Durethan 50%玻纤增强耐热老化稳定尼龙6塑料（18024445500）
PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized, improved surface finish
ISO Shortname: ISO 1874-PA6, GHR, 10-160, GF50
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.20
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.60
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.10
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 16400 11000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 220 140
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.5 4.3
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 10 15
Izod impact strength 23 °C kJ/m² ISO 180-1U 90 80
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10 20
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 10
Flexural modulus 2 mm/min MPa ISO 178-A 15000 11000
Flexural strength 2 mm/min MPa ISO 178-A 340 230
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3 4
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 220 |