PA6 BKV 35 CX H2.0 900876德国朗盛Durethan 35%玻纤增强尼龙6塑料（18024445500）
PA 6, 35 % glass fibers, injection molding, heat aging stabilized
ISO Shortname: ISO1874-PA 6, GHR, 10-100, GF35
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.2
C Molding shrinkage, transverse 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.7
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.15
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 10500 6500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 180 110
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 5.5
Izod impact strength 23 °C kJ/m² ISO 180-1U 70
Izod impact strength -30 °C kJ/m² ISO 180-1U 60
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10
Flexural modulus 2 mm/min MPa ISO 178-A 10000
Flexural strength 2 mm/min MPa ISO 178-A 280
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 270 |