PA6 BKV 30 G W1 901317德国朗盛Durethan 30%玻纤增强耐候级尼龙6塑料（18024445500）
PA 6, 30 % glass fibers, injection molding, weather stabilized
ISO Shortname: ISO 1874-PA 6, GLR, 14-100, GF30
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.2
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.6
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9900 6600
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 180 106
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.7 6.1
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 60 65
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 50 40
Izod impact strength 23 °C kJ/m² ISO 180-1U 50 60
Izod impact strength -30 °C kJ/m² ISO 180-1U 45 40
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10 10
Flexural modulus 2 mm/min MPa ISO 178-A 8700 6300
Flexural strength 2 mm/min MPa ISO 178-A 270 177
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.7 5.7
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 260 156
C Puncture maximum force 23 °C N ISO 6603-2 840
C Puncture maximum force -30 °C N ISO 6603-2 740
C Puncture energy 23 °C J ISO 6603-2 3.0
C Puncture energy -30 °C J ISO 6603-2 2.0
Ball indentation hardness N/mm² ISO 2039-1 209 |