PA6 BKV 30 EF 000000德国朗盛Durethan 30%玻纤增强低粘度易流动尼龙6塑料（18024445500）
PA 6, 30% glassfibres, injection molding grade, low viscosity (EasyFlow)
ISO Shortname:
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.168
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.738
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.037
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.148
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.226
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.578
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.049
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.143
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9300 5700
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 180 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.2 5.6
Izod impact strength 23 °C kJ/m² ISO 180-1U 55 65
Izod impact strength -40 °C kJ/m² ISO 180-1U 45 35
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10 15
Flexural modulus 2 mm/min MPa ISO 178-A 7800 5100
Flexural strength 2 mm/min MPa ISO 178-A 270 170
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.1 5.9
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 255 135 |