PA6 BKV 30 000000德国朗盛Durethan 30%玻纤增强尼龙6塑料（18024445500）
PA 6, 30 % glass fibers, injection molding
ISO/ ASTM
ISO Shortname: ISO 1874-PA 6, GR, 14-100, GF30
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Melt volume-flow rate 260 °C; 5 kg cm³/(10 min) ISO 1133-1 14
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.16
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.82
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.03
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.12
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9800 6100
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 180 105
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 6.0
C Tensile creep modulus 1 h MPa ISO 899-1 5100
C Tensile creep modulus 1000 h MPa ISO 899-1 4100
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 80 95
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 70 70
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15 20
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 75 80
Izod impact strength -30 °C kJ/m² ISO 180-1U 60 70
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15 20
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 10 10
Flexural modulus 2 mm/min MPa ISO 178-A 8600 5100
Flexural strength 2 mm/min MPa ISO 178-A 280 170
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 6.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 145
C Puncture maximum force 23 °C N ISO 6603-2 1071
C Puncture maximum force -30 °C N ISO 6603-2 950
C Puncture energy 23 °C J ISO 6603-2 8 14
C Puncture energy -30 °C J ISO 6603-2 6 5
Ball indentation hardness N/mm² ISO 2039-1 210 100 |