PA6 BKV 25 F30 000000德国朗盛Durethan 25%玻纤增强阻燃注塑级尼龙6塑料（18024445500）
PA 6, 25 % glass fibers, injection molding, flame retardant
ISO Shortname: ISO 1874-PA 6, GFHR, 14-110, GF25; ISO 1043-PA GF FR (17)
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.3
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.6
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 11000 7300
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 150 90
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.3 4.4
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 55 55
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 45 50
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 10 15
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 50 55
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 45 50
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A 10 15
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 10000 7000
Flexural strength 2 mm/min MPa ISO 178-A 230 155
Flexural strain at flexural strength 2 mm/min % ISO 178-A 2.5 4.0 |