PA6 BKV 230 DUS008 000000德国朗盛Durethan 30%玻纤增强耐冲击热老化稳定尼龙6塑料（18024445500）
PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized
ISO Shortname: ISO 1874-PA 6-HI, MR, 14-080, GF30
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.3
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.8
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.07
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.16
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 8500 4200
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 130 80
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 4.1 8.6
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 85 100
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 95 90
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 20 37
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 13 13
Izod impact strength 23 °C kJ/m² ISO 180-1U 75 95
Izod impact strength -30 °C kJ/m² ISO 180-1U 80 80
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 20 35
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 15 15
Flexural modulus 2 mm/min MPa ISO 178-A 7400 4200
Flexural strength 2 mm/min MPa ISO 178-A 205 125
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.8 6.6
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 190 100 |