PA6 BKV 20 FN20 000000德国朗盛Durethan 20%玻纤增强无卤阻燃尼龙6塑料（18024445500）
PA 6, 20 % glass fibers, injection molding, halogen free flame retardant
ISO Shortname: ISO 1874-PA 6, GFHR, 12-060, GF20; ISO 1043-PA GF FR (30)
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.6
C Molding shrinkage, transverse 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.7
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 6100 3100
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 100 55
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3 15
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 35 100
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 30
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10 <10
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 30 85
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 11
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 6100 3200
Flexural strength 2 mm/min MPa ISO 178-A 170 90
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.5 7
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 165 75 |