PA6 BKV 15 H2.0 DUS008 901510德国朗盛Durethan 15%玻纤增强热老化稳定尼龙6塑料(18024445500)
PA 6, 15 % glass fibers, injection molding, heat-aging stabilized
ISO Shortname: ISO 1874-PA 6, GHR, 14-070, GF15
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.5
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.8
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 6600 3100
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 120 59
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.4 12
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 35 100
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10 <10
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 40 90
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 35 40
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 10
Flexural modulus 2 mm/min MPa ISO 178-A 5700 2800
Flexural strength 2 mm/min MPa ISO 178-A 195 100
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.8 7.3
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 175 75
C Puncture maximum force 23 °C N ISO 6603-2 574
C Puncture maximum force -30 °C N ISO 6603-2 546
C Puncture energy 23 °C J ISO 6603-2 2.2
C Puncture energy -30 °C J ISO 6603-2 2.0 |