PA6 BKV 15 DUS008 000000德国朗盛Durethan 15%玻纤增强注塑级尼龙6塑料（18024445500）

PA 6, 15 % glass fibers, injection molding



ISO Shortname: ISO 1874-PA 6, GR, 14-060, GF15

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.35　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.59　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.13　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.16　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 6500 3100
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 130 65
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 12
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 50 100
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 45 45
Izod impact strength 23 °C kJ/m² ISO 180-1U 45 85
Izod impact strength -30 °C kJ/m² ISO 180-1U 40 40
Izod notched impact strength 23 °C kJ/m² ISO 180-1A <10 10
Flexural modulus 2 mm/min MPa ISO 178-A 5500 3100
Flexural strength 2 mm/min MPa ISO 178-A 205 110
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.3 8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 180 80
C Puncture maximum force 23 °C N ISO 6603-2 940