PA6 BKV 115 H2.0 DUS008 000000德国朗盛Durethan 15%玻纤增强耐热耐冲击尼龙6塑料（18024445500）
PA 6, 15% glass fibers, injection molding, improved impact strength, heat-aging stabilized
ISO Shortname: ISO 1874-PA 6-HI, GHR, 14-060, GF15
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.5
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.6
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.15
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 5900 3000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 115 60
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 4 12
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 65 100
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 45 45
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10 15
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10 <10
Charpy notched impact strength -40 °C kJ/m&sup2; ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 55 85
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 40 45
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A <10 15
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 5200 2900
Flexural strength 2 mm/min MPa ISO 178-A 185 100
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.5 7
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 165 80
C Puncture maximum force 23 °C N ISO 6603-2 710
C Puncture maximum force -30 °C N ISO 6603-2 590
C Puncture energy 23 °C J ISO 6603-2 3
C Puncture energy -30 °C J ISO 6603-2 2.2 |