PA 6, 15% glass fibers, injection molding, improved impact strength
ISO Shortname: ISO 1874-PA 6-HI, GR, 14-060, GF15
Property Test Condition Unit Standard guide value
d.a.m. cond.
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 5600 2800
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 115 65
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 4 12
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 65 80
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 50
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA 10
Flexural modulus 2 mm/min MPa ISO 178-A 4900 2500
Flexural strength 2 mm/min MPa ISO 178-A 185 95
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5 8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 165 70
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 220
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 195
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 215
Other properties (23 °C)
C Density kg/m&sup3; ISO 1183 1228
Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 280
C Injection molding-Mold temperature °C ISO 294 80 |