PA6 BC 304 H3.0 000000德国朗盛Durethan耐热老化稳定冲击强度改进尼龙6塑料（18024445500）
PA 6, non-reinforced, injection molding, improved impact strength, heat-aging stabilized
ISO/ ASTM
ISO Shortname: ISO 1874 PA 6-HI, GHR, 14-020
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 260 °C / MT 80 °C; 500 bar % acc. ISO 2577 1.14
Molding shrinkage, transverse 150x105x3; 260 °C / MT 80 °C; 500 bar % acc. ISO 2577 1.45
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.38
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.46
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 1800 800
C Yield stress 50 mm/min MPa ISO 527-1,-2 45 35
C Yield strain 50 mm/min % ISO 527-1,-2 4.5 30
C Nominal strain at break 50 mm/min % ISO 527-1,-2 > 50 > 50
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N N
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 85 120
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 20 20
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 70 100
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 30 17
Flexural modulus 2 mm/min MPa ISO 178-A 1600 700
Flexural strength 2 mm/min MPa ISO 178-A 60 30
Flexural strain at flexural strength 2 mm/min % ISO 178-A 7.0 9.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 55 25
C Puncture energy 23 °C J ISO 6603-2 120 125 |