PA6 B 40 SK 000000德国朗盛Durethan风机叶片插头用尼龙6塑料(18024445500)
PA 6, non-reinforced, injection molding
ISO/ ASTM
ISO Shortname: ISO 1874-PA 6, GR, 22-030
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.9
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.96
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.21
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.2
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 3200 900
C Yield stress 50 mm/min MPa ISO 527-1,-2 85 40
C Yield strain 50 mm/min % ISO 527-1,-2 4.0 25
C Nominal strain at break 50 mm/min % ISO 527-1,-2 20 > 50
C Tensile creep modulus 1 h MPa ISO 899-1 700
C Tensile creep modulus 1000 h MPa ISO 899-1 570
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N N
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA < 10 50
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m&sup2; ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U N N
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U N N
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A < 10 < 10
Izod notched impact strength -40 °C kJ/m&sup2; ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 2800 800 |