PA6 PX11311沙伯基础创新LNP™ KONDUIT™ PX11311 compound导热矿物填充(18024445500)
General Information
Product Description
Thermally conductive mineral filled PA6 FR compound
Also known as: LNP* KONDUIT* Compound PX11311
Product reorder name: PX11311
General
Material Status Commercial: Active
Availability Asia Pacific
Filler / Reinforcement Mineral
Features Flame Retardant
Thermally Conductive
Processing Method Injection Molding
ASTM & ISO Properties 1
Physical Nominal Value Unit Test Method
Density 1.74 g/cm³ ASTM D792
Melt Volume-Flow Rate (MVR) (300°C/10.0 kg) 2.99 in³/10min ISO 1133
Molding Shrinkage - Flow (24 hr) 3.3E-3 in/in ASTM D955
Molding Shrinkage - Across Flow (24 hr) 4.8E-3 in/in ASTM D955
Water Absorption (73°F, 24 hr) 0.25 % Internal Method
Water Absorption (Equilibrium, 73°F, 50% RH) 0.040 % ISO 62
Mechanical Nominal Value Unit Test Method
Tensile Modulus 2 1.05E+6 psi ASTM D638
Tensile Strength 3 (Break) 7540 psi ASTM D638
Tensile Elongation 3 (Break) 2.0 % ASTM D638
Flexural Modulus 4 (1.97 in Span) 1.31E+6 psi ASTM D790
Flexural Strength 4 (Break, 1.97 in Span) 11000 psi ASTM D790
Impact Nominal Value Unit Test Method
Charpy Unnotched Impact Strength 2.5 to 8.7 ft·lb/in² ISO 179
Notched Izod Impact (73°F) 0.81 ft·lb/in ASTM D256
Unnotched Izod Impact (73°F) 3.4 ft·lb/in ASTM D4812
Thermal Nominal Value Unit Test Method
Deflection Temperature Under Load (264 psi, Unannealed, 0.252 in) 390 °F ASTM D648
CLTE - Flow ASTM E831
-40 to 104°F 1.7E-5 in/in/°F
104 to 248°F 1.1E-5 in/in/°F
CLTE - Transverse ASTM E831
-40 to 104°F 2.6E-5 in/in/°F
104 to 248°F 3.9E-5 in/in/°F
Specific Heat 0.339 Btu/lb/°F ASTM C351
Thermal Conductivity ASTM E1461
-- 5 8.3 Btu·in/hr/ft²/°F
-- 6 15 Btu·in/hr/ft²/°F
Thermal Conductivity ISO 22007-2
-- 7 6.9 Btu·in/hr/ft²/°F
-- 8 9.6 Btu·in/hr/ft²/°F
Electrical Nominal Value Unit Test Method
Surface Resistivity > 1.0E+15 ohm ASTM D257
Dielectric Strength (0.0394 in, in Oil) > 250 V/mil ASTM D149
Dielectric Constant (1.10 GHz) 4.74 ASTM ES7-83
Dissipation Factor (1.10 GHz) 7.7E-3 ASTM ES7-83
Comparative Tracking Index 600 V IEC 60112
High Amp Arc Ignition (HAI) PLC 0 UL 746
Hot-wire Ignition (HWI) PLC 0 UL 746 |