PA66 49美国首诺Vydyne®冲击改性通用级尼龙66塑料（18024445500）
Physical Dry Conditioned Unit Test Method
Density 1.11 -- g/cm³ ISO 1183
Molding Shrinkage ISO 294-4
Across Flow : 2.00 mm 1.6 -- %
Flow : 2.00 mm 1.8 -- %
Water Absorption (23°C, 24 hr) 1.3 -- % ISO 62
Water Absorption (Equilibrium, 50% RH) 2.3 -- % ISO 62
Mechanical Dry Conditioned Unit Test Method
Tensile Modulus 3040 2130 MPa ISO 527-2
Tensile Stress (Yield) 70.0 50.0 MPa ISO 527-2
Tensile Stress (Break) 46.0 42.0 MPa ISO 527-2
Tensile Strain (Break) 17 40 % ISO 527-2
Flexural Modulus 2600 890 MPa ISO 178
Flexural Stress 81.0 27.0 MPa ISO 178
Charpy Notched Impact Strength ISO 179
-40°C 8.0 6.0 kJ/m²
-30°C 11 10 kJ/m²
23°C 13 43 kJ/m²
Charpy Unnotched Impact Strength ISO 179
-30°C No Break No Break
23°C No Break No Break
Notched Izod Impact Strength ISO 180
-40°C 8.0 10 kJ/m²
-30°C 9.0 15 kJ/m²
23°C 10 37 kJ/m²
Thermal Dry Conditioned Unit Test Method
Heat Deflection Temperature ISO 75-2/B
0.45 MPa, Unannealed 202 -- °C
Heat Deflection Temperature ISO 75-2/A
1.8 MPa, Unannealed 69.0 -- °C
Melting Temperature 260 -- °C ISO 11357-3
CLTE - Flow (23 to 55°C, 2.00 mm) -- cm/cm/°C ISO 11359-2
CLTE - Transverse (23 to 55°C, 2.00 mm) -- cm/cm/°C ISO 11359-2
RTI Elec UL 746
0.750 mm 125 -- °C
1.50 mm 125 -- °C
3.00 mm 125 -- °C
RTI Imp UL 746
0.750 mm 75.0 -- °C
1.50 mm 75.0 -- °C
3.00 mm 75.0 -- °C
RTI Str UL 746
0.750 mm 85.0 -- °C
1.50 mm 85.0 -- °C
3.00 mm 85.0 -- °C
Volume Resistivity (0.750 mm) -- ohm·cm IEC 60093
Dielectric Strength (1.00 mm) 23 -- kV/mm ASTM D149
Arc Resistance (3.00 mm) PLC 5 -- ASTM D495
Comparative Tracking Index (3.00 mm) 600 -- V IEC 60112
High Amp Arc Ignition (HAI) UL 746
0.750 mm PLC 0 --
1.50 mm PLC 0 --
3.00 mm PLC 0 --
High Voltage Arc Tracking Rate (HVTR) PLC 1 -- UL 746
Hot-wire Ignition (HWI) UL 746
0.750 mm PLC 4 --
1.50 mm PLC 4 --
3.00 mm PLC 3 --
Flammability Dry Conditioned Unit Test Method
Flame Rating UL 94
0.750 mm HB --
1.50 mm HB --
3.00 mm HB --
Glow Wire Flammability Index IEC 60695-2-12
0.750 mm 700 -- °C
1.50 mm 750 -- °C
3.00 mm 700 -- °C
Glow Wire Ignition Temperature IEC 60695-2-13
0.750 mm 725 -- °C
1.50 mm 775 -- °C
3.00 mm 725 -- °C
Injection Dry Unit
Drying Temperature 80.0 °C
Drying Time 4.0 hr
Suggested Max Regrind 25 %
Rear Temperature 280 to 310 °C
Middle Temperature 280 to 310 °C
Front Temperature 280 to 310 °C
Nozzle Temperature 280 to 310 °C
Processing (Melt) Temp 285 to 305 °C
Mold Temperature 65.0 to 95.0 °C |