PA66 A 218W V30 NATURAL法国罗地亚TECHNYL 30%玻纤增强热稳定电磁阀用尼龙66塑料（18024445500）
TECHNYL A 218W V30 NATURAL
Properties
Typical values of properties are for natural grades
Standards Unit Values
d.a.m. Cond.
Physical
Water absorption(24h at 23°C) ISO 62 % 0,80
Density ISO 1183/A g/cm3 1,35
Molding shrinkage Parallel RHODIA % 0,50
Molding shrinkage normal or perpendicular RHODIA % 0,80
Molding Shrinkage Isotropy RHODIA 0,62
Mechanical
Tensile Modulus ISO 527 Type 1A MPa 10000 6600
Tensile strength at break ISO 527 Type 1A MPa 190 135
Elongation at break ISO 527 Type 1A % 3,20 4
Flexural modulus ISO 178 MPa 9000 6500
ASTM D-790 MPa 8600
Flexural maximum stress ASTM D-790 MPa 270
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 11 15
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 85 95
Izod notched impact strength (23 °C) ISO 180/1A kJ/m2 10 17
ASTM D256 J/m 105
Flammability
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 HB
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 700
Thermal
Melting Temperature ISO 11357 °C 262
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 254
Heat deflection temperature (1,82 MPa) ASTM D-648 °C 250
Coef of Linear thermal expansion normal or ISO 11359 E-5/°C 2,8
perpendicular (23°C to 85°C)
Coef of Linear thermal expansion parallel (23°C to ISO 11359 E-5/°C 2,8
85°C)
Electrical
Comparative tracking index (Sol A) IEC 60112 V 600 600
Dielectric strength IEC 60243 kV/mm 35 40
Dissipation factor IEC 60250 0,020 0,080
Relative permittivity IEC 60250 3,70 4,30
Surface resistivity IEC 60093 Ohm 1E 14 1E 12
Volume resistivity IEC 60093 Ohm/cm 1E 15 1E 12 |