PA66 A 218W V30 BLACK FA法国罗地亚TECHNYL® 30%玻纤增强热稳定耐水解尼龙66塑料（18024445500）
TECHNYL® A 218W V30 BLACK FA
The values of properties are for black grade.
Properties Standards Unit Values
d.a.m*. Cond.**
Physical
Water absorption (24 h at 23°C) ISO 62 % 0.80 -
Density ISO 1183-A g/cm3 1.35 -
Molding shrinkage Parallel (1) (RHODIA-EP) RHODIA-EP % 0.5 -
Molding shrinkage normal or perpendicular (1) (Rhodia EP) RHODIA-EP % 0.80 -
Molding Shrinkage Isotropy (Rhodia EP) RHODIA-EP 0.62 -
Mechanical
Tensile modulus ISO 527 type 1 A MPa 10000 7500
Elongation at break ISO 527 type 1 A % 3 4
Tensile strength at break ISO 527 type 1 A MPa 185 130
Flexural modulus ISO 178 MPa 9000 6400
Flexural maximum stress ISO 178 MPa 275 180
Charpy notched impact strength ISO 179/1eA kJ/m2 11 15
Charpy unnotched impact strength ISO 179/1eU kJ/m2 80 90
Izod notched impact strength ISO 180/1A kJ/m2 10 17
Flamability
Flammability UL 94 (Thickness 0,8 mm) ISO 1210/UL 94 HB -
Flammability UL 94 (Thickness 1,6 mm) ISO 1210/UL 94 HB -
Flammability UL 94 (Thickness 3,2 mm) ISO 1210/UL 94 HB -
Glow wire flammability index (thickness = 1,6) IEC60695-2-12 °C 700 -
Thermal
Melting Temperature ISO 11357 °C 263 -
Heat deflection temperature, 1,8 Mpa ISO 75/Af °C 255 -
Coef. of Linear thermal expansion parallel (23°C to 85°C) ISO 11359 E-5 / °C 2.80 -
Electrical
Relative permittivity IEC60250 3.70 3.30
Dissipation factor IEC60250 0.02 0.08
Volume resistivity IEC60093 Ohm.cm 10E14 10E11
Surface resistivity IEC60093 Ohm 10E13 10E11
Dielectric strength IEC60243 kV/mm 35 -
Comparative tracking index sol. A IEC60112 Volt 600 - |